Structural and optical analysis of Zn-1 (-) xCdxO nanopowder synthesized by Hydrothermal method
|
|
|
| 【文章作者】Sui, Y. R.;Cao, Y.;Li, X. F.;Yue, Y. G.;Yao, B.;Li, X. Y.;Lang, J. H.;Yang, J. H. |
| 【文章摘要】 Zn-1 (-) xCdxO nanopowder in a wide range of Cd contents has been obtained by hydrothermal synthesis method. Synthesized nanopowder was characterized by powder X-ray diffraction, X-ray photoelectron spectroscopy, Transmission electron microscopy and Photoluminescence. As x varies from 0 to 1, it was observed that the crystal structure changes from wurtzite (ZnO) to mixture of wurtzite and cubic, and finally to cubic (CdO) structure. The wurtzite-type structure of ZnO can be stabilized up to nominal Cd content x similar to 0.1 without cubic CdO phase separation. For the Zn-1 (-) xCdxO nanopowder with wurzite structure, a significant change was observed in ultra-violet near-band-edge emission with variation in Cd content x. The change is attributed to the direct modulation of band gap caused by Zn/Cd substitution. (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved. |
| 【关 键 字】 |
|
【卷】41 【ISSUE】1 Pt.A 【ISSUEID】815C0073
【文章期份】2015
【发布日期】2016/1/20 0:00:00
点击率：3
打印
关闭
|
|