Fabrication of complex shaped ceramic parts with surface-oxidized Si3N4 powder via digital light processing based stereolithography method
【文件类型】 【消费金额】1.5 【文章页数】5 【会员操作】  
【文章作者】Huang, Rong-Ji;Jiang, Qiang-Guo;Wu, Hai-Dong;Li, Yan-Hui;Liu, Wen-Yong;Lu, Xin-Xin;Wu, Shang-Hua
【文章摘要】      Si3N4 ceramic is difficultly fabricated by digital light processing (DLP) based stereolithography method, due to a large refractive index difference between Si3N4 powder and resin. In this paper, a surface oxidation approach of Si3N4 powder for improving cure depth is proposed. The results showed that, the amorphous SiO2 layer was uniformly attached onto the surface of Si3N4 powder by surface oxidation, and the absorbance of Si3N4 powder decreased as increasing oxidation degree. Moreover, the cure depth of the suspension significantly increased because of a smaller absorbance and a refractive index difference at the interface between oxidized Si3N4 powder and resin. At the exposure energy of 500 mJ/cm(2), the cure depth of the raw Si3N4 powder was 34 mu m. After oxidizing at 1150 degrees C and 1200 degrees C for 1 h, the cure depth effectively increased to 42 mu m and 51 mu m, respectively. Finally, the complex-shaped Si3N4 parts were successfully fabricated using surface-oxidized Si3N4 powder via DLP method.
【关 键 字】
【卷】45【ISSUE】4【ISSUEID】815C0073    【文章期份】2019    【发布日期】2019/8/27 11:25:43    点击率:0    打印    关闭
关于我们 公告信息 业务资费 广告合同 友情链接 购买阅读卡 在线订《水泥》
网络市场部:010-65761182 网络技术部:010-51164639  传真:010-65761182 Email:service@chinabmi.com
在线咨询:  
国家建筑材料工业局技术图书馆 京ICP备06011358号   京公网安备11010502024146