Facile synthesis of a novel flower-like BiFeO3 microspheres/graphene with superior electromagnetic wave absorption performances
【文件类型】 【消费金额】2.4 【文章页数】8 【会员操作】  
【文章作者】Gao, Xiang;Wang, Yan;Wang, Qiguan;Wu, Xinming;Zhang, Wenzhi;Zong, Meng;Zhang, Lijuan
【文章摘要】      In recent years, porous or layered magnetic materials have received increasing attention due to their low density and lightweight. In this work, porous BiFeO3 microspheres and three-dimensional porous BiFeO3 microsphere-reduced graphene oxide (RGO) composite (3D porous BiFeO3/RGO) were prepared by one-step etching processing using pure BiFeO3 particles as precursors. The precursor undergoes dissolution-recrystallization/reduction process, resulting in large amount of BiFeO3 fragments and graphene hybrid product, which forms 3D porous BiFeO3/RGO composite. Electromagnetic (EM) absorption performance measurements exhibit that at low thickness of 1.8 mm, porous BiFeO3/RGO composite can achieve reflection loss (R-L) value up to -46.7 dB and absorption bandwidth (defined by R-L < -10 dB) exceeding 4.7 GHz (from 12.0 to 16.7 GHz), testifying outstanding microwave absorbing performance. Compared with pure porous BiFeO3, improved EM wave absorption ability of as-prepared porous BiFeO3/RGO composite is attributed to interfacial polarization, multiple reflections, scattering, and appropriate impedance matching.
【关 键 字】
【卷】45【ISSUE】3【ISSUEID】815C0073    【文章期份】2019    【发布日期】2019/8/27 11:26:07    点击率:0    打印    关闭
关于我们 公告信息 业务资费 广告合同 友情链接 购买阅读卡 在线订《水泥》
网络市场部:010-65761182 网络技术部:010-51164639  传真:010-65761182 Email:service@chinabmi.com
在线咨询:  
国家建筑材料工业局技术图书馆 京ICP备06011358号   京公网安备11010502024146