Effects of sintering parameters and Nd doping on the microwave dielectric properties of Y2O3 ceramics
|
|
|
| 【文章作者】Zhang, Xiaorong;Fan, Guifen;Wang, Xiaohong;Lei, Wen;Fei, Liang;Lu, Wenzhong |
| 【文章摘要】 Y2O3 ceramics with good dielectric properties were prepared via co-precipitation reaction and subsequent sintering in a muffle furnace. The effects of Nd doping and sintering temperature on microwave dielectric properties were studied. With the increase in sintering temperature, the density, quality factor (Q x f), and dielectric constant (epsilon(r)) values of pure Y2O3 ceramics increased to the maximum and then gradually decreased. The Y2O3 ceramics sintered at 1500 degrees C for 4 h showed optimal dielectric properties: epsilon(r) = 10.76, Q x f = 82, 188 GHz, and tau(f) = 54.4 ppm/degrees C. With the addition of Nd dopant, the Q x f values, epsilon(r) and tau(f) of the Nd: Y2O3 ceramics apparently increased, but excessive amount degraded the quality factor. The Y2O3 ceramics with 2 at% Nd2O3 sintered at 1460 degrees C displayed good microwave dielectric properties: epsilon(r) = 10.4, Q x f = 94, 149 GHz and tau(f) = -46.2 ppm/degrees C. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved. |
| 【关 键 字】 |
|
【卷】42 【ISSUE】7 【ISSUEID】815C0073
【文章期份】2016
【发布日期】2016/8/11 17:03:42
点击率：0
打印
关闭
|
|