Chemical synthesis, compositional, morphological, structural, optical and magnetic properties of Zn1-xDyxS nanoparticles
|
|
|
| 【文章作者】Poornaprakash, B.;Poojitha, P. T.;Chalapathi, U.;Ramu, S.;Vijayalakshmi, R. P.;Park, Si-Hyun |
| 【文章摘要】 Zn1-xDyxS (x = 0, 0.02 and 0.04) nanoparticles (NPs) were synthesized by chemical refluxing technique at 100 degrees C. The prepared samples were analyzed by studying their compositional, morphological, structural, optical and magnetic properties. EDS analysis confirmed the presence of zinc, dysprosium and sulfur in the samples in near stoichiometric ratio. The X-ray diffraction patterns do not show any Dy related peaks for the as-synthesized ZnS nanoparticles. The average diameter of the particles confirmed by TEM studies, was in the range 2-4 nm. Raman studies revealed that all the samples are single phase and exhibit cubic structure. From DRS studies, the band-gap was found to be in the range of 3.85-3.70 eV. All the doped ZnS nanoparticles exhibit ferromagnetic behavior with the Curie temperature higher than room temperature and the magnetic properties of doped ZnS nanoparticles depend on the concentration of Dy ions. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved. |
| 【关 键 字】 |
|
【卷】42 【ISSUE】7 【ISSUEID】815C0073
【文章期份】2016
【发布日期】2016/8/11 17:03:42
点击率：0
打印
关闭
|
|