Spectroscopic and laser properties of Ho3+ doped lanthanum-tungsten-tellurite glass and fiber
|
|
|
| 【文章作者】Li, Dahai;Xu, Wenbin;Kuan, Peiwen;Li, Wentao;Lin, Zhiquan;Wang, Xin;Zhang, Lei;Yu, Chunlei;Li, Kefen |
| 【文章摘要】 The spectroscopic properties of 2-mu m emission in Ho3+-doped lanthanum-tungsten-tellurite glasses with different Ho2O3 concentrations were investigated. The strongest emission was observed in a glass sample doped with 0.5 mol% Ho2O3, with a fluorescence lifetime of 3.16 ms and a emission cross section of 6.97 x 10(-21) cm(2) at 2040 nm. For this composition, no obvious changes in the emission properties and fluorescence lifetime were observed at temperatures of 295-350 K. Using this 60TeO(2)-30WO(3)-9.5La(2)O(3)-0.5Ho(2)O(3) glass as a core material, Ho3+-doped double cladding fiber with a core diameter of 14 pm and a numerical aperture of 0.12 was developed. A maximum laser output power of 34 mW at 2040 nm was achieved with a 9-cm-long Ho3+-doped tellurite glass fiber. To the best of our knowledge, this study presents the first report on the 2-mu m laser output from a Ho3+-doped tellurite oxide glass fiber resonantly pumped by a 1.94 mu m Tm-fiber laser. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved. |
| 【关 键 字】 |
|
【卷】42 【ISSUE】8 【ISSUEID】815C0073
【文章期份】2016
【发布日期】2016/8/11 17:03:59
点击率：2
打印
关闭
|
|