STUDY ON PREPARATION, COMPLEX PERMITTIVITY,PERMEABILITY AND MICROWAVE PROPERTIES OF BaZn_zCo_(2-z)Fe_(16)O_(27)/SiO_2 MICROCRYSTALLINE GLASS CERAMICS
|
|
|
| 【文章作者】 |
| 【文章摘要】 <正> BaZnzCo2-zFe16O27/SiO2 microcrystalline glass ceramics with Z=0.0, 0.5, 0.8 and 1.1 were prepared at temperature 1200℃ for 5h by citrate sol-gel process. The complex dielectric constant and complex permeability of BaZnzCo2-zFe16 O27/SiO2-paraffin wax composites had been measured. Both the complex dielectric constant and dielectric loss exhibit almost no variation with frequency in 0.1-6.0GHz. The real part of permeability decreases with increasing frequency for all samples, and the imaginary part of permeability exhibits a clear resonance peak at 1.44GHz for Co2 W/SiO2, 1.32GHz for Zn0.5Co1.5 W/SiO2, 1.20GHz for Zn0.8Co1.2W/SiO2, and 1.08GHz for Zn1.1 Co0.9 W/SiO2. It is also showed that the content of zinc has a close effect on the magnetic properties of BaZnzCo2-zFe16O27/SiO2 microcrystalline glass ceramics, the greater the zinc content, the higher the values of imaginary part of permeability and magnetic loss. |
| 【关 键 字】 |
|
【期刊】Acta Metallurgica Sinica(English Letters)【卷】【ISSUE】【ISSUEID】
【文章期份】2003
【发布日期】
点击率：1
打印
关闭
|
|