Microstructure, Microsegregation, and Mechanical Properties of Directional Solidified Mg–3.0Nd–1.5Gd Alloy
|
|
|
| 【文章作者】Shaojun Liu;Guangyu Yang;Wanqi Jie; |
| 【文章摘要】 The microstructure, microsegregation, and mechanical properties of directional solidified Mg–3.0Nd–1.5Gd ternary alloys were experimentally studied. Experimental results showed that the solidification microstructure was composed of dendrite primary a(Mg) phase and interdendritic a(Mg) ? Mg12(Nd, Gd) eutectic and Mg5 Gd phase. The primary dendrite arm spacing k1 and secondary dendrite arm spacing k2 were found to be depended on the cooling rate R in the form k1= 8.0415 9 10-6R-0.279 and k2= 6.8883 9 10-6R-0.205, respectively, under the constant temperature gradient of40 K/mm and in the region of cooling rates from 0.4 to 4 K/s. The concentration profiles of Nd and Gd elements calculated by Scheil model were found to be deviated from the ones measured by EPMA to varying degrees, due to ignorance of the back diffusion of the solutes Nd and Gd within a(Mg) matrix. And microsegregation of Gd depended more on the growth rate, compared with Nd microsegregation. The directionally solidified experimental alloy exhibited higher strength than the non-directionally solidified alloy, and the tensile strength of the directionally solidified experimental alloy was improved,while the corresponding elongation decreased with the increase of growth rate. |
| 【关 键 字】 |
|
【期刊】Acta Metallurgica Sinica(English Letters)【卷】【ISSUE】【ISSUEID】
【文章期份】2014
【发布日期】2015/1/14 0:00:00
点击率：1
打印
关闭
|
|