| 【文章摘要】 The microstructure, hardness, and precipitate free zones(PFZ) of V55Ti30Ni15 alloys during heat treatment have been investigated in this study. The microstructure resulting from different heat treatment conditions has a great influence on hardness. The microstructure resulting from different heat treatment conditions has a great influence on hardness. Fine Ni Ti particles precipitate from the supersaturated V-matrix solid solution at 750 °C, increase in quantity until 800 °C, and then dissolve back into the V-matrix at 850 °C. The resultant hardness decreases with temperature until 800 °C, and then increases from 800 to 850 °C. The microstructure containing small Ni Ti precipitates resulting from the treatment of 18 h at800 °C has a good soft condition for workability. PFZ formed at the grain boundary of V-matrix during heat treatment was observed. Vacancies depletion in V-matrix maybe led to the formation of PFZ. |