| 【文章摘要】 Through in situ transmission electron microscopy observation on SUS304 metastable austenitic stainless steel during stretching at room temperature,it is found that e martensite plates were induced preferentially from the sites of dislocation pile-ups.With increasing deformation,some of ε thin martensite platelets disappear and reversibly transform toγ austenite without heating treatment,which is different from the previous result that ε martensite can entirely transform toα'martensite.Then,some of deformation twins appear and grow along the vertical direction of ε martensite due to(111)_γ⊥(1010)_ε.Moreover,it is directly observed that multiple transformation mechanisms via γ→ε→γ,γ→ε,γ→α′,γ→ε→α′,γ→ deformation twins →α′ can co-exist. |