Synthesis of Sodium Beta Alumina Films by Heat Treatment of Sodium Aluminum Oxides
【文件类型】 【消费金额】1.5 【文章页数】5 【会员操作】  
【文章作者】池晨;Hirokazu KATSUI;Takashi GOTO;
【文章摘要】      Sodium beta alumina(Na-β-alumina) films were synthesized by heat treatment of NaAl_6O_(9.5)and γ-NaA1O_2 films at temperatures of 1 373-1 573 K.Single-phase γ-NaA1O_2 and NaAl_6O_(9.5) films were prepared by laser chemical vapor deposition at the deposition temperatures of 976 and 1 100 K,respectively.Subsequent heat treatment of the films resulted in the formation of Na-β-alumina with α-Al_2O_3 at temperatures above 1 373 K for NaAl_6O_(9.5) and 1 473 K for γ-NaA1O_2.On heat treatment at temperatures of 1 473-1 573 K,the faceted morphology with terraces of the as-deposited(110)-oriented γ-NaAlO_2 films transformed to a porous morphology with platelet grains comprising Na-β-alumina and α-Al_2O_3.On heat treatment at temperatures of1 373-1 473 K,the pyramidal,faceted grains of as-deposited NaAl_6O_(9.5) films transformed to planer,shapeanisotropic morphology in the film of mixed Na-β-alumina and α-Al_2O_3.A dense morphology was observed in both the as-deposited and heat-treated NaAl_6O_(9.5) films.
【关 键 字】
【期刊】【卷】【ISSUE】【ISSUEID】    【文章期份】2016    【发布日期】2016/3/15 0:00:00    点击率:1    打印    关闭
关于我们 公告信息 业务资费 广告合同 友情链接 购买阅读卡 在线订《水泥》
网络市场部:010-65761182 网络技术部:010-51164639  传真:010-65761182 Email:service@chinabmi.com
在线咨询:  
国家建筑材料工业局技术图书馆 京ICP备06011358号   京公网安备11010502024146